Investment casting of TiAl alloys
Umshaus, Josef ; Malec, Silvestr (referee) ; Zemčík, Ladislav (advisor)
Intermetallic alloys gama TiAl are prospective materials of future thanks its excellent machanical qualities and low density. However this alloy clash with for wider expansion to the practice on burdensomeness production and processing. Among disavantages belongs to also her bad fluidity. The diploma work is angaged in possibilities imporing fluidity alloys TiAl by the help of centrifuge casting. Casting healthy casts was achieved in experimental part.
|
|
| |
|
|
Investment casting of TiAl alloys
Umshaus, Josef ; Malec, Silvestr (referee) ; Zemčík, Ladislav (advisor)
Intermetallic alloys gama TiAl are prospective materials of future thanks its excellent machanical qualities and low density. However this alloy clash with for wider expansion to the practice on burdensomeness production and processing. Among disavantages belongs to also her bad fluidity. The diploma work is angaged in possibilities imporing fluidity alloys TiAl by the help of centrifuge casting. Casting healthy casts was achieved in experimental part.
|
|
| |
|
|
Interaction between TiAl melt and coated oxide refractories
Dočekalová, Kateřina ; Dlouhý, Antonín ; Zemčík, L. ; Fiala, J.
The present study focuses on reactions between ceramic crucibles and molten TiAl intermetallics. Coating strategies are investigated that exhibit a potential in slowing down the decomposition of the crucible wall. Uncoated crucibles (system TiAl melt - Al2O3 crucible) and crucibles with the coat (system TiAl melt - CaO coat - Al2O3 crucible) were used in melting and casting experiments. The reference state of the coated crucible before the melting trial was also investigated. Results of the SEM, EDAX and X-ray diffraction analysis contributed to the identification of the reaction zone and its chemical composition. The melt contamination with oxide inclusions results from the erosion process in which individual components of the melt diffuse along grain boundaries of the refractory and activate chemical reactions that decompose the crucible wall. Assessment of thermodynamic parameters associated with the chemical reactions helped in identifying the nature of the erosion process.
|
|
|
Vakuová metalurgie intermetalik TiAl
Zemčík, L. ; Dlouhý, Antonín ; Król, S. ; Pražmowski, M.
To be able to melt successfully type gamma TiAl alloys it is absolutely necessary to solve the fundamental metallurgical problems associated with the reactions between the melt and the refractories of crucibles and ceramic moulds, with the reactions between the melt and residual gases in the furnace chamber, and with the evaporation of aluminium from the melt. The paper deals with the physico - chemical analyses of the above processes and gives their evaluation based on the results of experimental melts of the type of Ti48Al2Cr2Nb1B (at.%) obtained in vacuum induction furnace. The work also gives the results of oxidation tests for the Ti48Al2Cr2Nb1B(at.%) alloy.
|